Interaction of a piezoelectric screw dislocation with a blunt mode III crack in a piezoelectric material (Englisch)
- Neue Suche nach: Song, H. P.
- Neue Suche nach: Gao, C. F.
- Neue Suche nach: Song, H. P.
- Neue Suche nach: Gao, C. F.
In:
ENGINEERING FRACTURE MECHANICS
;
96
;
687-700
;
2012
-
ISSN:
- Aufsatz (Zeitschrift) / Print
-
Titel:Interaction of a piezoelectric screw dislocation with a blunt mode III crack in a piezoelectric material
-
Beteiligte:Song, H. P. ( Autor:in ) / Gao, C. F. ( Autor:in )
-
Erschienen in:ENGINEERING FRACTURE MECHANICS ; 96 ; 687-700
-
Verlag:
- Neue Suche nach: Elsevier Science B.V., Amsterdam.
-
Erscheinungsdatum:01.01.2012
-
Format / Umfang:14 pages
-
ISSN:
-
Medientyp:Aufsatz (Zeitschrift)
-
Format:Print
-
Sprache:Englisch
- Neue Suche nach: 620.1 / 126
- Weitere Informationen zu Dewey Decimal Classification
-
Klassifikation:
-
Datenquelle:
© Metadata Copyright the British Library Board and other contributors. All rights reserved.
Inhaltsverzeichnis – Band 96
Zeige alle Jahrgänge und Ausgaben
Die Inhaltsverzeichnisse werden automatisch erzeugt und basieren auf den im Index des TIB-Portals verfügbaren Einzelnachweisen der enthaltenen Beiträge. Die Anzeige der Inhaltsverzeichnisse kann daher unvollständig oder lückenhaft sein.
- 1
-
Influence of loading rate on the delamination response of untufted and tufted carbon epoxy non-crimp fabric composites/Mode IIColin de Verdiere, M. / Skordos, A.A. / Walton, A.C. / May, Michael et al. | 2011
- 11
-
Influence of loading rate on the delamination response of untufted and tufted carbon epoxy non crimp fabric composites: Mode IColin de Verdiere, M. / Skordos, A.A. / May, M. / Walton, A.C. et al. | 2012
- 26
-
Modeling of mode-I fatigue crack growth in quasibrittle structures under cyclic compressionEliáš, Jan / Le, Jia-Liang et al. | 2012
- 37
-
Determination of the J integral for laminated double cantilever beam specimens: The curvature approachRask, M. / Sørensen, B.F. et al. | 2012
- 49
-
Tension and shear cracking during indentation of ductile materials by opposed wedgesBai, Yuanli / Atkins, Tony et al. | 2012
- 61
-
Strain gradient effects on steady state crack growth in rate-sensitive materialsNielsen, K.L. / Niordson, C.F. / Hutchinson, J.W. et al. | 2012
- 72
-
Mixed-mode crack initiation at the edge of Cu/Si interface due to nanoscale stress concentrationKishimoto, Kohei / Yan, Yabin / Sumigawa, Takashi / Kitamura, Takayuki et al. | 2012
- 82
-
The use of cyclic @DJ"@r as a parameter for fatigue initiation of X52 steelCapelle, J. / Predan, J. / Gubeljak, N. / Pluvinage, G. et al. | 2012
- 82
-
The use of cyclic ΔJρ as a parameter for fatigue initiation of X52 steelCapelle, J. / Predan, J. / Gubeljak, N. / Pluvinage, G. et al. | 2012
- 96
-
Determination of the Paris law constants in round bars from beach marks on fracture surfacesBranco, R. / Antunes, F.V. / Costa, J.D. / Yang, Feng Peng / Kuang, Zhen Bang et al. | 2012
- 107
-
Characterization of timber fracture using the Digital Image Correlation technique and Finite Element MethodDubois, F. / Méité, M. / Pop, O. / Absi, J. et al. | 2012
- 122
-
Two-parameter characterization of elastic–plastic crack front fields: Surface cracked plates under uniaxial and biaxial bendingWang, Xin et al. | 2012
- 147
-
Two-stage planar approximation of non-planar crack growthHombal, V.K. / Ling, Y. / Wolfe, K.A. / Mahadevan, S. et al. | 2012
- 165
-
Fracture and fragmentation of quartz and albite during single-diamond sliding-point contactHogan, James D. / Rogers, Robert J. / Spray, John G. / Boonsue, Suporn et al. | 2012
- 179
-
A deformation-mechanism-based energy partitioning approach for measurement of plane-stress fracture toughness of low-density polyethyleneJar, P.-Y.B. / Cao, W. et al. | 2012
- 192
-
Toughness of a patterned interface between two elastically dissimilar solidsCordisco, Fernando A. / Zavattieri, Pablo D. / Hector, Louis G. Jr. / Bower, Allan F. et al. | 2012
- 209
-
Fracture resistance curve over the complete mixed-mode I and II range for 5083 aluminum alloyYang, Wuchao / Qian, Xudong et al. | 2012
- 226
-
Nonuniform ferroelastic domain switching driven by two-parameter crack tip stress fieldCui, Yuanqing / Zhong, Zheng et al. | 2012
- 241
-
Nonlinear fracture analysis of single-layer graphene sheetsBaykasoglu, Cengiz / Mugan, Ata et al. | 2012
- 251
-
Evaluation of constraint effects on creep crack growth by experimental investigation and numerical simulationZhao, Lei / Jing, Hongyang / Xu, Lianyong / Han, Yongdian / Xiu, Junjie et al. | 2012
- 267
-
Crack growth resistance behavior of lanthanum doped bismuth ferrite–lead titanate: Effect of tetragonality and mixed phase crystal structuresLeist, Thorsten / Brötz, Joachim / Seo, Yo-Han / Cheng, Shumeng / Webber, Kyle G. et al. | 2012
- 276
-
Investigation of fracture in small-scale SENT tests of a welded X80 pipeline steel using Digital Image Correlation with node splittingFagerholt, E. / Østby, E. / Børvik, T. / Hopperstad, O.S. et al. | 2012
- 294
-
Acoustic emission during fracture toughness tests of SA333 Gr.6 steelMukhopadhyay, C.K. / Sasikala, G. / Jayakumar, T. / Raj, Baldev et al. | 2012
- 307
-
Closed-form structural stress and stress intensity factor solutions for spot welds in square overlap parts of cross-tension specimensSripichai, K. / Pan, J. et al. | 2012
- 328
-
J-integral based fracture toughness of 15Cr–5Ni stainless steel during phase transformationJikai, Liu / Coret, M. / Combescure, A. / Chaudet, P. et al. | 2012
- 340
-
On the prediction of fatigue life in double shear lap joints including interference fitted pinChakherlou, T.N. / Taghizadeh, H. / Mirzajanzadeh, M. / Aghdam, A.B. et al. | 2012
- 355
-
A general approach to fracture analysis of tapered bonded joints and doublersDuong, C.N. et al. | 2012
- 380
-
Damage detection of rubber toughened nanocomposites in the fracture process zone using carbon nanotubesCardoso, Shane M. / Chalivendra, Vijaya B. / Shukla, Arun / Yang, Sze et al. | 2012
- 392
-
Small scale yielding conditions for steep residual stress distributionYasuoka, Tetsuo / Mizutani, Yoshihiro / Todoroki, Akira et al. | 2012
- 401
-
Determination of fracture toughness of AZ31 Mg alloy using the cohesive finite element methodGuo, X. / Chang, K. / Chen, L.Q. / Zhou, M. et al. | 2012
- 416
-
Determination of the fracture parameters of the Double-K model using weight functions of split-tension specimensInce, Ragip et al. | 2012
- 433
-
Fracture behaviour and toughening mechanism in Zanchor reinforced composites under mode I loadingKusaka, Takayuki / Watanabe, Keiko / Hojo, Masaki / Fukuoka, Toshiyasu / Ishibashi, Masayasu et al. | 2011
- 447
-
Three-dimensional simulation of fretting crack nucleation and growthCarter, B.J. / Schenck, E.C. / Wawrzynek, P.A. / Ingraffea, A.R. / Barlow, K.W. et al. | 2012
- 461
-
A stress-based criterion for ductile crack initiation of pre-strained carbon steelKamaya, Masayuki et al. | 2012
- 480
-
Experimental validation of edge strength model for glass with polished and cut edge finishingVandebroek, Marc / Belis, Jan / Louter, Christian / Van Tendeloo, Gustaaf et al. | 2012
- 490
-
Modeling crack propagation for advanced 4-point bending testing of metal–dielectric thin film stacksGadelrab, K.R. / Chiesa, M. / Hecker, M. / Engelmann, H.-J. et al. | 2012
- 500
-
The interrelation of the parameters in the Paris equation of fatigue crack growthLi, Yazhi / Wang, Hai / Gong, Dezhi et al. | 2012
- 510
-
An investigation on fatigue crack growth rates through a designed nonsymmetric crack growth testHe, Xiaofan / Tan, Mingyi / Xing, Jing Tang et al. | 2012
- 528
-
Design of an in situ mechanical test for spot-welded jointsPayen, G.R. / Klöcker, H. / Lens, A. / Wilkinson, D.S. / Embury, J.D. et al. | 2012
- 539
-
An engineering model for rapid crack propagation along fluid pressurized plastic pipeLeevers, Patrick et al. | 2012
- 558
-
Consideration of elastic follow-up in the treatment of combined primary and secondary stresses in fracture assessmentsAinsworth, R.A. et al. | 2012
- 570
-
Fracture analysis of girth welded pipelines with 3D embedded cracks subjected to biaxial loading conditionsYi, Dake / Xiao, Zhong Min / Idapalapati, Sridhar / Kumar, Shashi Bhushan et al. | 2012
- 588
-
Prediction of remaining useful life for fatigue-damaged structures using Bayesian inferenceKarandikar, Jaydeep M. / Kim, Nam Ho / Schmitz, Tony L. et al. | 2012
- 606
-
The mechanical crack tip opening displacement fracture criterion in piezoelectric ceramicsXue, Cun / Yong, Huadong / Zhou, Youhe et al. | 2012
- 615
-
Interlaminar fracture characterization of woven glass/epoxy composites under mixed-mode II/III loading conditions at cryogenic temperaturesMiura, Masaya / Shindo, Yasuhide / Takeda, Tomo / Narita, Fumio et al. | 2012
- 626
-
Stress intensity factors and fatigue growth of a surface crack in a drill pipe during rotary drilling operationDao, Ngoc Ha / Sellami, Hedi et al. | 2012
- 641
-
Development of a new fracture test to identify the critical energy release rate: The Tensile Flexure test on Notched SpecimenVandellos, Thomas / Hautier, Mathieu / Carrere, Nicolas / Huchette, Cédric et al. | 2012
- 656
-
Experimental study on fracture performance of ultra-high toughness cementitious composites with J-integralLiu, Wen / Xu, Shilang / Li, Qinghua et al. | 2012
- 667
-
Experimental investigation of deformation and failure mechanisms in rock under indentation by digital image correlationZhang, Hao / Huang, Ganyun / Song, Haipeng / Kang, Yilan et al. | 2012
- 676
-
Mixed mode delamination growth of multidirectional composite laminates under fatigue loadingPeng, Lei / Xu, Jifeng / Zhang, Jianyu / Zhao, Libin et al. | 2012
- 687
-
Interaction of a piezoelectric screw dislocation with a blunt mode III crack in a piezoelectric materialSong, Hao-Peng / Gao, Cun-Fa et al. | 2012
- 701
-
Thermo-hydro-mechanical modeling of impermeable discontinuity in saturated porous media with X-FEM techniqueKhoei, A.R. / Moallemi, S. / Haghighat, E. et al. | 2012
- 724
-
Evaluation of bone cohesive laws using an inverse method applied to the DCB testPereira, F.A.M. / Morais, J.J.L. / de Moura, M.F.S.F. / Dourado, N. / Dias, M.I.R. et al. | 2012
- 737
-
Mixed-mode partition theories for one-dimensional delamination in laminated composite beamsHarvey, C.M. / Wang, S. et al. | 2012
- 760
-
Some comments on the paper: Review of fracture toughness and standards (EFM, 2012, vol. 85, 1–46)Schijve, Jaap et al. | 2012
- 762
-
Verification of a continuum mechanical explanation of plasticity-induced crack closure under plain strain conditions by means of finite element analysisFischlschweiger, Michael / Ecker, Werner / Pippan, Reinhard et al. | 2012
- IFC
-
Editorial Board| 2012