The flow-stress behavior at hot-working temperatures and strain rates of the powder-metallurgy superalloy LSHR was determined under nominally-isothermal and transient-heating conditions. Two conventional methods, compression of right-circular cylinders and torsion of thin-walled tubes, were used for isothermal tests. A direct-resistance-heating technique utilizing torsion of round-bar specimens in a Gleeble machine was applied for both isothermal and transient-heating conditions. When expressed in terms of effective stress and strain, baseline data determined by the two conventional methods showed good agreement. With the aid of a flow-localization analysis to assess the confounding influence of axial (and radial) temperature gradients on deformation uniformity, the flow stresses determined from nominally-isothermal Gleeble torsion tests were shown to be broadly similar to those from the conventional tests. With regard to transient phenomena, Gleeble tests were also useful in quantifying the effect of rapid heating and short soak time.