Insulation resistance (IR) degradation in Ni-BaTiO3 multilayer ceramic capacitors has been characterized by the measurement of both time to failure and direct-current (DC) leakage current as a function of stress time under highly accelerated life test conditions. The measured leakage current-time dependence data fit well to an exponential form, and a characteristic growth time ?SD can be determined. A greater value of tau(sub SD) represents a slower IR degradation process. Oxygen vacancy migration and localization at the grain boundary region results in the reduction of the Schottky barrier height and has been found to be the main reason for IR degradation in Ni-BaTiO3 capacitors. The reduction of barrier height as a function of time follows an exponential relation of phi (??)=phi (0)e(exp -2?t), where the degradation rate constant ??=??o??(????/????) is inversely proportional to the mean time to failure (MTTF) and can be determined using an Arrhenius plot. For oxygen vacancy electromigration, a lower barrier height phi(0) will favor a slow IR degradation process, but a lower phi(0) will also promote electronic carrier conduction across the barrier and decrease the insulation resistance. As a result, a moderate barrier height phi(0) (and therefore a moderate IR value) with a longer MTTF (smaller degradation rate constant ??) will result in a minimized IR degradation process and the most improved reliability in Ni-BaTiO3 multilayer ceramic capacitors.