A comparison of the reciprocating sliding wear behaviour of steel based metal matrix composites processed from self-propagating high-temperature synthesised Fe-TiC and Fe-TiB2 masteralloys (Englisch)
- Neue Suche nach: Degnan, C.C.
- Neue Suche nach: Shipway, P.H.
- Neue Suche nach: Degnan, C.C.
- Neue Suche nach: Shipway, P.H.
In:
Wear - An International Journal on the Science and Technology of Friction, Lubrication and Wear
;
252
, 9/10
;
832-841
;
2002
-
ISSN:
- Aufsatz (Zeitschrift) / Print
-
Titel:A comparison of the reciprocating sliding wear behaviour of steel based metal matrix composites processed from self-propagating high-temperature synthesised Fe-TiC and Fe-TiB2 masteralloys
-
Beteiligte:Degnan, C.C. ( Autor:in ) / Shipway, P.H. ( Autor:in )
-
Erschienen in:
-
Verlag:
-
Erscheinungsdatum:2002
-
Format / Umfang:10 Seiten, 13 Bilder, 27 Quellen
-
ISSN:
-
DOI:
-
Medientyp:Aufsatz (Zeitschrift)
-
Format:Print
-
Sprache:Englisch
-
Schlagwörter:
-
Datenquelle:
Inhaltsverzeichnis – Band 252, Ausgabe 9/10
Zeige alle Jahrgänge und Ausgaben
Die Inhaltsverzeichnisse werden automatisch erzeugt und basieren auf den im Index des TIB-Portals verfügbaren Einzelnachweisen der enthaltenen Beiträge. Die Anzeige der Inhaltsverzeichnisse kann daher unvollständig oder lückenhaft sein.
- 679
-
Effect of counterface roughness on abrasive wear of hydroxyapatiteKalin, Mitjan et al. | 2002
- 686
-
Application of molybdenum complexes of 1-aryl-2,5-dithiohydrazodicarbonamides as extreme pressure lubricant additivesRastogi, R.B. et al. | 2002
- 693
-
Sliding wear of cast zinc-based alloy bearings under static and dynamic loading conditionsSavaskan, T. et al. | 2002
- 704
-
Multi-scale polymer properties with applications to solid lubricants in ironingHuang, Chen-Hsi et al. | 2002
- 711
-
Tribological and corrosion wear of graphite ring against Ti6Al4V disk in artificial sea waterSerre, I. et al. | 2002
- 719
-
The statistical correlation of the coefficient of friction and wear rate of PTFE composites with steel counterface roughness and hardnessWieleba, Wojciech et al. | 2002
- 730
-
An integrated intelligence system for wear debris analysisPeng, Zhongxiao et al. | 2002
- 744
-
A tribo-electrochemical apparatus for in vitro investigation of fretting-corrosion of metallic implant materialsBarril, S. et al. | 2002
- 755
-
Effect of phase stability on the wear resistance of white cast iron at 800(degree)CXing, Jian-Dong et al. | 2002
- 755
-
Effect of phase stability on the wear resistance of white cast iron at 800 deg CXing, Jian-Dong / Gao, Yi-Min / Wang, En-Ze / Bao, Chong-Gao et al. | 2002
- 761
-
Tribological performance of nano-thin fluoropolymer coated slidersMa, Yansheng et al. | 2002
- 769
-
Abrasive wear performance of various polyamidesRajesh, J.John et al. | 2002
- 777
-
Extremely low coefficient of friction of diamond sliding against Ag thin films on Si(1 1 1) surface under ultrahigh vacuum conditionGoto, Minoru et al. | 2002
- 787
-
Flaking failure in rolling contact fatigue caused by indentations on mating surface (I)Fujii, Y. / Maeda, K. et al. | 2002
- 787
-
Flaking failure in rolling contact fatigue caused by indentations on mating surface (I) - Reproduction of flaking failure accompanied by cracks extending bi-directionally relative to the load-movementFujii, Yukio et al. | 2002
- 799
-
Flaking failure in rolling contact fatigue caused by indentations on mating surface (II)Fujii, Y. / Maeda, K. et al. | 2002
- 799
-
Flaking failure in rolling contact fatigue caused by indentations on mating surface (II) - Formation process of flaking failure accompanied by cracks extending bi-directionally relative to the load-movementFujii, Yukio et al. | 2002
- 811
-
Flaking failure in rolling contact fatigue caused by indentations on mating surface (III)Fujii, Y. / Maeda, K. et al. | 2002
- 811
-
Flaking failure in rolling contact fatigue caused by indentations on mating surface (III) - Mechanism of crack growth in the direction opposite to the load-movementFujii, Yukio et al. | 2002
- 824
-
Friction and wear behavior of flame-sprayed PEEK coatingsLi, Jianfeng et al. | 2002
- 832
-
A comparison of the reciprocating sliding wear behaviour of steel based metal matrix composites processed from self-propagating high-temperature synthesised Fe-TiC and Fe-TiB2 masteralloysDegnan, C.C. et al. | 2002
- 842
-
Comments on 'Fractal or fiction' by D.J. Whitehouse (Wear 249 (2001) 345-353)Greenwood, J.A. et al. | 2002
-
CONTENTS LIST| 2002