To evaluate the masking ability of IPS e. max all-ceramics system of HO series. IPS e. max Press HO ingots were fabricated into twenty cylindrical specimens (n=5) with the diameter of 13mm and four different thinknesses (0.4mm, 0.6mm, 0.8mm, 1.0mm). All specimens after veneered, gazed and cemented to metal substrate disks (thickness 3mm, diameter 13mm) were measured on both the white background and metal substrate disks background using a spectrophotometer and values of L, a and b were calculated to compare color differences among four groups. Meanwhile ΔE with the preselected required color (A2 color) were calculated. ΔE<1.5 was considered a clinically acceptable color match. In the 0.4mm thickness specimens group, the values of L, a and b significantly increased (-1.36±0.05, -0.15±0.06, -1.46±0.02, respectively) between the white background and abutment background. But there were no significant color differences in the other three groups (P<0.05). In the 0.6mm and 0.8mm thicknesses specimens groups, the color difference values (0.71±0.04, 1.14±0.06, respectively) with A2 color were less than the defined value. Thus the cylindrical specimens with the thickness of 0.6mm, 0.8mm and 1.0mm could mask the metal substrate disks background sufficiently and the thickness of 0.6mm and 0.8mm had an acceptable color match compared with the target color. IPS e. max all-ceramics system of HO series can produce clinically acceptable color match and have the capacity to mask a dark background such as a dark tooth or core buildup material.