Extensive material and device statistics of performance and reproducibility are presented to show the maturity of this technology. The demonstration vehicles to monitor yields during this demonstration were long-wavelength infrared (LWIR) HgCdTe multilayer wafers with 128 x 128 detector arrays. The heterostructure photodetectors were of the p-on-n planar configuration. Device data show that MBE LWIR diode test structures have performance that equals that of p-on-n double heterostructure photodiodes made by LPE. Due to the special attention given to understanding and reducing epilayer growth-induced defects, the authors have achieved improvements in FPA operability values from 92 & to 98 %. These improvements have resulted in the demonstration of a 128 x 128 FPA hybrid that had detectivity (D) background limited performance when operating at 80 K in a tactical background environment. Mean D was 1.28 x 1011cmHz1/2/W. The corresponding mean NEDeltaT was an excellent 5.9 mK.