On the use of non-iterative methods in cohesive fracture (Englisch)
- Neue Suche nach: Alfaiate, J.
- Weitere Informationen zu Alfaiate, J.:
- https://orcid.org/0000-0001-7046-7499
- Neue Suche nach: Sluys, L. J.
- Neue Suche nach: Alfaiate, J.
- Weitere Informationen zu Alfaiate, J.:
- https://orcid.org/0000-0001-7046-7499
- Neue Suche nach: Sluys, L. J.
In:
International Journal of Fracture
;
210
, 1-2
; 167-186
;
2018
-
ISSN:
- Aufsatz (Zeitschrift) / Print
-
Titel:On the use of non-iterative methods in cohesive fracture
-
Beteiligte:Alfaiate, J. ( Autor:in ) / Sluys, L. J. ( Autor:in )
-
Erschienen in:International Journal of Fracture ; 210, 1-2 ; 167-186
-
Verlag:
- Neue Suche nach: Springer Netherlands
- Neue Suche nach: Kluwer Academic Publ.
-
Erscheinungsort:Dordrecht [u.a.]
-
Erscheinungsdatum:2018
-
ISSN:
-
ZDBID:
-
DOI:
-
Medientyp:Aufsatz (Zeitschrift)
-
Format:Print
-
Sprache:Englisch
- Neue Suche nach: 51.32
- Weitere Informationen zu Basisklassifikation
- Neue Suche nach: 535/5110
-
Schlagwörter:
-
Klassifikation:
-
Datenquelle:
Inhaltsverzeichnis – Band 210, Ausgabe 1-2
Zeige alle Jahrgänge und Ausgaben
Die Inhaltsverzeichnisse werden automatisch erzeugt und basieren auf den im Index des TIB-Portals verfügbaren Einzelnachweisen der enthaltenen Beiträge. Die Anzeige der Inhaltsverzeichnisse kann daher unvollständig oder lückenhaft sein.
- 1
-
Improving the fracture toughness of 3D printed thermoplastic polymers by fused deposition modelingGardan, Julien / Makke, Ali / Recho, Naman et al. | 2017
- 17
-
Fast crack propagation correlated with crack tip stress in 2D hexagonal atomic latticesYang, Xiujin / Tian, Hong / Zhang, Bin et al. | 2017
- 29
-
A localization analysis of a non-uniform damage lattice in presence of strength gradientHérisson, Benjamin / Challamel, Noël / Picandet, Vincent / Perrot, Arnaud et al. | 2018
- 45
-
Appraisement of planar, bending and twisting cracks in 3D with isotropic and orthotropic damage modelsBarbat, G. B. / Cervera, M. / Chiumenti, M. et al. | 2018
- 81
-
Surface effects on delamination of a thin film bonded to an elastic substrateYang, Y. / Lee, K. Y. / Li, X.-F. et al. | 2018
- 95
-
Gradient piezoelectricity for cracks under an impact loadSladek, Jan / Sladek, Vladimir / Wünsche, Michael / Kasala, Jozef et al. | 2018
- 113
-
Achieving pervasive fracture and fragmentation in three-dimensions: an unstructuring-based approachSpring, Daniel W. / Paulino, Glaucio H. et al. | 2018
- 137
-
Influence of pressure cycling on damage evolution in an unfilled EPDM exposed to high-pressure hydrogenOno, Hiroaki / Nait-Ali, Azdine / Kane Diallo, Ousseynou / Benoit, Guillaume / Castagnet, Sylvie et al. | 2018
- 153
-
Scaling of brittle failure: strength versus toughnessBrochard, Laurent / Souguir, Sabri / Sab, Karam et al. | 2018
- 167
-
On the use of non-iterative methods in cohesive fractureAlfaiate, J. / Sluys, L. J. et al. | 2018
- 187
-
Energy release rate approximation for edge cracks using higher-order topological derivativesAlidoost, Kazem / Geubelle, Philippe H. / Tortorelli, Daniel A. et al. | 2018
- 207
-
A theoretical resistance-curve based on nonproportional plastic strainUnger, David J. et al. | 2018
- 213
-
Static mode fatigue crack propagation and generalized stress intensity correlation for fatigue–brittle polymersFurmanski, Jevan / Pruitt, Lisa A. et al. | 2018
- 223
-
Interfacial fracture strength evaluation of Cu/SiN micro-components: applicability of the linear fracture mechanics criterion under a hydrogen environmentTakahashi, Yoshimasa / Ashida, Itaru / Arai, Shigeo / Higuchi, Kimitaka / Yamamoto, Yuta / Muto, Shunsuke et al. | 2018