TEM observation of the initial stages of oxidation on TiAl and TiAl-0.2Zr intermetallic compounds (Japanisch)
- Neue Suche nach: Fujimoto, S.
- Neue Suche nach: Kato, T.
- Neue Suche nach: Taniguchi, S.
- Neue Suche nach: Shibata, T.
- Neue Suche nach: Fujimoto, S.
- Neue Suche nach: Kato, T.
- Neue Suche nach: Taniguchi, S.
- Neue Suche nach: Shibata, T.
In:
Journal of the Japan Institute of Metals
;
64
, 7
;
502-507
;
2000
-
ISSN:
- Aufsatz (Zeitschrift) / Print
-
Titel:TEM observation of the initial stages of oxidation on TiAl and TiAl-0.2Zr intermetallic compounds
-
Weitere Titelangaben:TEM Untersuchung des Anfangsstadiums der Oxidation von TiAl und der intermetallischen Verbindung TiAl-0.2Zr
Titel japanisch -
Beteiligte:Fujimoto, S. ( Autor:in ) / Kato, T. ( Autor:in ) / Taniguchi, S. ( Autor:in ) / Shibata, T. ( Autor:in )
-
Erschienen in:Journal of the Japan Institute of Metals ; 64, 7 ; 502-507
-
Verlag:
-
Erscheinungsdatum:2000
-
Format / Umfang:6 Seiten, 9 Bilder, 2 Tabellen, 18 Quellen
-
ISSN:
-
Medientyp:Aufsatz (Zeitschrift)
-
Format:Print
-
Sprache:Japanisch
-
Schlagwörter:Titanaluminid , Zirkoniumzusatz , Oxidationsbeständigkeit , Aluminiumoxid , Titanoxid , chemische Zusammensetzung , intermetallische Phase , AES (Auger-Elektronenspektrometrie) , REM (Rasterelektronenmikroskopie) , Elektronenstrahlmikrosonde , Gefüge (Werkstoff) , TEM (Transmissionselektronenmikroskopie) , Titanaluminiumlegierung
-
Datenquelle:
Inhaltsverzeichnis – Band 64, Ausgabe 7
Zeige alle Jahrgänge und Ausgaben
Die Inhaltsverzeichnisse werden automatisch erzeugt und basieren auf den im Index des TIB-Portals verfügbaren Einzelnachweisen der enthaltenen Beiträge. Die Anzeige der Inhaltsverzeichnisse kann daher unvollständig oder lückenhaft sein.
- 483
-
Solifification structure of functionally graded hypereutectic Al-Ni alloys produced by centrifugal duplex castingOhmi, T. / Ueda, M. / Itoh, Y. / Matsuura, K. / Kudoh, M. et al. | 2000
- 490
-
Corrosion behavior of ion nitrided stainless steels containing MoChoe, H.C. / Hwang, K.Y. / Kim, K.H. et al. | 2000
- 502
-
TEM observation of the initial stages of oxidation on TiAl and TiAl-0.2Zr intermetallic compoundsFujimoto, S. / Kato, T. / Taniguchi, S. / Shibata, T. et al. | 2000
- 508
-
Mixing of oxygen in titanium nitride films formed by reactive HCD ion platingMiura, K. / Ishigami, I. / Mizukoshi, T. et al. | 2000
- 518
-
Production of fine-microstructural nickel aluminides by wet mechanical alloying processDoi, Y. / Akimoto, H. / Matsuki, K. / Aida, T. / Ochiai, S. et al. | 2000
- 535
-
Effect of cross slips on multiple slips and recrystallization in (111) and (001) Al single crystalsTagami, M. / Kashihara, K. / Okada, T. / Inoko, F. et al. | 2000
- 543
-
Corrosion behavior of diamond-like carbon coated on aluminum in sodium chloride solutionTsuchiyama, A. / Minami, M. / Takatani, Y. / Hayashi, Y. / Masuda, M. / Hasuyama, H. et al. | 2000
- 551
-
Effect of Al-Fe-Si ternary intermetallic compounds on initiation and propagation of pitting attacks for industrial aluminum 1100Seri, O. / Satoh, K. / Furumata, K. et al. | 2000
- 559
-
Solid-solution strengthening and high-temperature compressive strength of Nb-X alloys (X = Ta, V, Mo and W)Tan, Y. / Tanaka, H. / Ma, C. / Kasama, A. / Tanaka, R. / Mishima, Y. / Hanada, S. et al. | 2000
- 566
-
Solid-solution strengthening and high-temperature compressive ductility of Nb-Mo-W ternary alloysTan, Y. / Tanaka, H. / Ma, C. / Kasama, A. / Tanaka, R. / Mishima, Y. / Hanada, S. et al. | 2000
- 584
-
Relationship between crack propagation rate and dissolution rate of type 310 stainless steel in H2SO4-NaCl solutionKamide, H. / Komagata, H. et al. | 2000